Abstract
Recently, was proposed a chemical method for preparation of ferroelectric thin films based on oxide precursors. In this work, PZT thin films were prepared to attest the viability of this method for cation-substitution. In this study, a small concentration of Nb (5 mol%) was selected as substitute of B-site in ABO 3 structure of PZT. Dielectric and ferroelectric properties of PZT films were studied as a function of cation-substitution. Results for Nb-PZT were compared with PZT films undoped. The values of dielectric constant, at typical 100 kHz frequency, were 358 and 137, for PZT and Nb-PZT films respectively. Remanent polarizations of these films were respectively 7.33 w C/cm 2 and 13.3 w C/cm 2 , while the measured coercive fields were 101 kV/cm and 93 kV/cm. As a result, changes on observed dielectric and ferroelectric values confirm the Nb substitution in PZT thin film produced by oxide precursor method.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call