Abstract

We have performed proton irradiation of W and W-5wt.%Ta materials at 350 °C with a step-wise damage level increase up to 0.7 dpa and using two beam energies, namely 40 keV and 3 MeV, in order to probe the accumulation of radiation-induced lattice damage in these materials. Interstitial-type a/2 <111> dislocation loops are formed under irradiation, and their size increases in W-5Ta up to a loop width of 21 ± 4 nm at 0.3 dpa, where loop saturation takes place. In contrast, the loop length in W increases progressively up to 183 ± 50 nm at 0.7 dpa, whereas the loop width remains relatively constant at 29 ± 7 nm at >0.3 dpa, giving rise to dislocation strings. The dislocation loops and tangles are observed in both materials examined after a 3 MeV proton irradiation at 350 °C. Ta doping delays the evolution of radiation-induced dislocation structures in W, and can consequently impact the hydrogen isotope retention under plasma exposure.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.