Abstract
In recent years, surgical procedures for hip prostheses have increased. These implants are manufactured with materials with high stiffness compared to the bone, causing bone loss or aseptic loosening. This research proposes an alternative structural composite consisting of 3D-printing polylactic acid layers and carbon fiber laminates (PLA/CFRC) with potential application in prosthetic implants. Fourier-transform infrared spectroscopy (FTIR) achieved to characterize starting materials and structural composites revealed secondary chemical interactions between the carbonyl group of PLA with the hydroxyl group of epoxy resin from CFRC. Thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) results show both components (PLA and CFRC) influence the structural composite's thermal behavior, observed in the temperatures of degradation, glass transition, and melting. Furthermore, the composite reached cell viability above 80%, a tensile modulus of 19.29 ± 0.48 GPa and tensile strength of 238.91 ± 25.95 MPa, with mechanical properties very similar to the bone. The results of this study demonstrated that the proposed PLA/CFRC composite can be used as candidate base material for the manufacturing of a hip femoral stem prostheses.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.