Abstract
In-plane structural anisotropy is characteristic of nonpolar (1120) a-plane GaN (a-GaN) films grown on r-plane sapphire substrates. The anisotropic peak broadenings of X-ray rocking curves (XRCs) are clearly observed with M- or W-shaped dependence on the azimuth angles. We investigated the optical properties of both M- and W-shaped a-GaN samples with room and low-temperature photoluminescence (PL) measurements. The W-shaped a-GaN film showed higher PL intensity and more compressive strain compared to the M-shaped a-GaN film, whereas the XRC peak widths of the M-shaped a-GaN film on the azimuth angles are lower than those of W-shaped specimens, indicating that better crystalline quality was obtained. We speculate that the PL intensity and strain state of a-GaN layers may be more influenced by the crystallinity of a specific crystal orientation or direction, especially along the m-axis as opposed to the c-axis. This occurrence is most likely due to anisotropic defect distributions, resulting from differences in dangling bond densities of (0001) and {1-100} facets.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.