Abstract
ABSTRACTThin films of Co substituted ZnO and ZnCo2O4 were deposited on c-axis (0001) oriented Al2O3 substrates using pulsed laser deposition. The XRD results showed all the films were highly (002) oriented with a less intense peak of (311) for ZnCo2O4 thin film. Micro-Raman spectra of ceramic targets showed the modes related to wurtzite ZnO and spinel ZnCo2O4 structures. In thin films of Zn1−xCoxO no modes corresponding to ZnCo2O4 were detected. The intensity of E1(LO) and multiphonon peak at 584 and 540 cm−1 respectively, increased with increase in Co substitution. The optical absorption of the films showed that the band gap decreased with increase of Co concentrations at room temperature along with the sub-bandgap absorptions due to d-d transitions of Co2+. Similar sub-bandgap d-d transition was also observed in the absorption spectra ZnCo2O4 thin films. The highest saturated magnetization (0.2μB/Co) was obtained for 5%Co substituted ZnO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.