Abstract
Mid-infrared intersubband transitions are investigated in nonpolar m-plane and a-plane GaN/AlGaN multi-quantum well heterostructures. Nominally identical heterostructures were grown by ammonia molecular-beam epitaxy on free-standing m-plane and a-plane GaN substrates. A total of 12 well- and barrier-doped samples with intersubband transition energies in the range of 220–320 meV (wavelength range 3.8–5.6 μm) were grown. The intersubband absorption lines of the m-plane samples were 10–40% narrower than those of the a-plane samples, and a very narrow intersubband absorption linewidth of 38 meV (full width at half maximum) at a transition energy of approximately 250 meV (5 μm wavelength) was observed in an m-plane sample. Narrower intersubband absorption linewidths of m-plane samples can be explained by more abrupt heterostructure interfaces revealed by structural characterization, which is attributed to a higher stability of the m-plane compared to the a-plane. No significant difference in the intersubband absorption linewidth was observed between the barrier- and well-doped samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.