Abstract
Selective laser sintering (SLS) technique is capable of rapidly fabricating customized implants with porous structure. A simple encapsulation process was developed to coat 316L stainless steel (316L SS) powder with ethylene-vinyl acetate copolymer (EVA). Subsequently, porous 316L SS was prepared by SLS preforming of EVA-coated metal powders, debinding and sintering in hydrogen atmosphere. The effects of processing parameters on pore characteristics and mechanical properties were analyzed. The results indicate that the porosity of green body mainly depends on laser energy density, while the pore features and mechanical properties of sintered specimens are largely dominated by sintering temperature. After sintering at 1100–1300°C, the average pore size and porosity are 160–35μm and 58–28%, respectively. In addition, the elastic modulus and compressive yield strength are 1.58–6.64GPa and 15.5–52.8MPa, respectively. It is revealed that the pore structural parameters and mechanical properties of the as-sintered porous 316L SS can be controlled readily to match with those of cancellous bone by modification of SLS processing parameters and subsequent sintering temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.