Abstract
Bismuth ferrite (BiFeO3, short for BFO) powders were prepared at low temperature using sol-gel process. Single-phase BiFeO3 powders with distorted perovskite structure were obtained after calcining at 600°C. According to the Scherrer formula the calculated crystallite size (D XRD) is about 39 nm. The value of the average particle size (D BET) is larger than that of D XRD. A typical magnetic hysteresis loop was observed at room temperature, indicating that the BiFeO3 nanoparticles show a weak ferromagnetic order. The remnant magnetization (2M r) and coercive field (2H C) are 0.033 emu/g and 395 Oe, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.