Abstract

Two mixed ferrite systems, namely Ni0.65Zn0.35 Fe2O4 (Ni-Zn) and Mn0.75 Zn0.18 Fe2.07 O4 (Mn-Zn) have been prepared by coprecipitation method, and then the resulting ultrafine powders were heat treated at different temperatures from 200 to 800degC for improved crystallinity and magnetic properties. The samples were characterized by X-ray diffraction, vibrating sample magnetometry, and ferromagnetic resonance spectrometry. As a result of the heat treatment, the average particle size has been found to increase from 9.9 to 15.7 nm for Ni-Zn ferrites and from 2.4 to 10.2 nm for Mn-Zn ferrites, and the corresponding magnetization values have increased from 9.1 to 23 emu/g for Ni-Zn ferrites and from 7.9 to 11.7 emu/g for Mn-Zn ferrites, respectively. The results are discussed in the light of changes in particle size and inversion degree parameter for cationic distribution at nanoscales

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.