Abstract
The structure-function relationship of composite films obtained from soybean-protein isolate (SPI) and cod gelatin was studied. Films with different ratios of SPI:gelatin (0, 25, 50, 75, 100% [w/w]) and plasticized by a mixture of glycerol and sorbitol were prepared by casting. Regardless of the soybean-protein concentration, the thickness and water-vapor permeability of the composite films diminished significantly as compared to pure-gelatin films. The formulation containing 25% SPI: 75% cod-skin gelatin had the maximum force at the breaking point, which was 1.8-fold and 2.8-fold greater than those of 100% gelatin and 100% SPI films, respectively. Moreover, this formulation offered high percent-deformation values lower than those of gelatin but higher than all other films containing SPI-, and the same relatively low water-vapor permeability as the 100% SPI film. While all the films exhibited high water solubility, a slight reduction in film solubility and soluble protein was observed with increasing SPI concentration. Differential-scanning calorimetry analyses revealed that gelatin was completely denatured in all films, while soy proteins largely maintained their native conformation. Analysis by fourier-transform–infrared spectroscopy revealed that the presence of 25% SPI produced gelatin conformational changes, self-aggregation of gelatin chains, and intermolecular associations via C O bonds between gelatin and SPI proteins. All films were translucent in appearance, but the yellowish color increased with increasing proportions of the soybean proteins.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.