Abstract
We describe the growth of thin films of Ta 2O 5 on quartz and silicon (1 0 0) substrates by an in situ photo-assisted pulsed laser deposition (photo-PLD) using radiation from a Nd:YAG laser (wavelength, λ=532 nm ) to stimulate the ablation, and from an excimer lamp to excite additional photochemistry. The layers grown were investigated by Fourier transform infrared (FT-IR) spectroscopy, UV spectrophotometry, atomic force microscopy (AFM), ellipsometry and electrical measurements. We have found that they exhibit a significant improvement in microstructure, and optical and electrical properties compared with conventional PLD films prepared under, otherwise, identical conditions. For example, FT-IR results showed that the suboxide content in the as-grown films deposited by the photo-PLD process is less, while the leakage current density was an order of magnitude less at around 10 −6 A/cm 2 at a bias of 1 V. These results indicate that this photo-PLD process approach can be advantageous for dielectric and optical oxide film growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.