Strong metal support interaction (SMSI) and MoO3 synergistic effect of Pt-based catalysts on the promotion of CO activity and sulfur resistance.

Abstract

In industrial applications, Pt-based catalysts for CO oxidation have the dual challenges of CO self-poisoning and SO2 toxicity. This study used synthetic Keggin-type H3PMo12O40 (PMA) as the site of Pt, and the Pt-MoO3 produced by decomposition of PMA was anchored to TiO2 to construct the dual-interface structure of Pt-MoO3 and Pt-TiO2, abbreviated as Pt-P&M/TiO2. Pt-0.125P&M/TiO2 with a molar ratio of Pt to PMA of 8:1 showed both good CO oxidation activity and SO2 tolerance. In the CO activity test, the CO complete conversion temperature T100 of Pt-0.125P&M/TiO2 was 113 ℃ (compared with 135 ℃ for Pt/TiO2). In the SO2 resistance test, the conversion efficiency of Pt-0.125P&M/TiO2 at 170 ℃ remained at 60% after 72h, while that of Pt/TiO2 was only 13%. H2-TPR and XPS tests revealed that lattice oxygen provided by TiO2 and hydroxyl produced by MoO3 increased the CO reaction rate on Pt. According to the DFT theoretical calculation, the electronegative MoO3 attracted the d-orbital electrons of Pt, which reduced the adsorption energy of CO and SO2 from - 4.15eV and - 2.54eV to - 3.56eV and - 1.52eV, respectively, and further weakened the influence of strong CO adsorption and SO2 poisoning on the catalyst. This work explored the relationship between catalyst structure and catalyst performance and provided a feasible technical idea for the design of high-performance CO catalysts in industrial applications.