Abstract
A simple and scalable "dip and dry" method was developed for fabricating stretchable polyurethane sponge-based polymer composite with excellent shear stiffening effect, creep resisting and adhesion property. The stiffness of the composite was tunable, the storage modulus (G') could automatically increase 3 orders of magnitude with the increasing of shear frequency, and the G'max could reach to as high as 1.55 MPa. Importantly, the composite with ideal damping capacity reduced the impact force by 2 orders of magnitude even under 26 cycles of consecutive dynamic impact loading with no obvious mechanical degradation. Moreover, an enhancing mechanism was proposed and it was found the "B-O cross bond" and the entanglement of polymer chains were attributed to the shear stiffening characteristic. Finally, the excellent adhesion ability and hydrophobicity guarantee the composite with reliable mechanical performance and longer lifespan.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.