Abstract
Stress corrosion cracking (SCC) is a common cause of structural failure. The simultaneous action of the corrosive environment and tensile stresses creates cracks that have an intercrystalline or transcrys-talline character. These are cracks with a fragile morphology of the fracture surface without signs of plastic deformation in their vicinity. SCC cracks occur in several alloys. This paper focuses on copper alloys in which this type of failure occurs frequently. Examples from practice show cases where the occurrence of SCC violation was related to the conditions of use of components and their production technologies. The paper does not aim to capture all the influences associated with the occurrence of SCC failure of copper alloy products.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.