Abstract
The aim of this study was to evaluate, in vitro, the biaxial flexural strength (ISO 6872) of a feldspathic ceramic (VM7, Vita Zahnfabrik) coated with a resin cement with different thicknesses and polymerization mode. Control groups consisted in VM7 with and without acid etching with 10% hydrofluoric acid for 1 min. Experimental groups comprised VM7 etched, silanated and coated with Variolink II (Ivoclar Vivadent) cement, that was polymerized through the porcelain in light-cure and dual-cure modes, with thickness ≤150 µm or >150 µm. The specimens (n=15) were subjected to the biaxial flexural strength essay and analyzed fractographically. Parametric (Dunnet, Anova 2-way, Tukey) and non-parametric tests (Weibull) were used to evaluate results. Ceramic disks coated with resin cements of either activation modes and thicknesses exhibited higher flexural strength while the Weibull moduli did not present significant differences for a confidence interval of 95%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.