Abstract
a-SiNx:H thin films of different stoichiometry grown by PECVD were subjected to irradiation by 100 MeV Au8+ ions with various fluences to understand the effect of stoichiometry on properties of thin films upon irradiation. Ellipsometry and UV–Vis study suggest the variation in the refractive index of thin films with fluence. The evolution of Hydrogen due to irradiation is quantified with the help of ERDA. RBS was probed to study the change in thin films' composition upon irradiation, which further helps understand the change in thin films' optical properties. Quenching of photoluminescence in the films with all stoichiometries was also observed due to ion irradiation. X-TEM images show the formation of discontinuous ion tracks of radius 2.5 nm in the film closer to silicon nitride stoichiometry. However, Si rich film does not show the clear formation of tracks. Results are explained in the framework of the Thermal spike mechanism of ion-solid interaction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.