Abstract
AbstractA series of thermally stable organic/inorganic second‐order nonlinear optical (NLO) composites via sequential self‐repetitive reaction (SSRR) and sol–gel process has been developed. This SSRR is based on carbodiimide (CDI) chemistry. The difunctional azo chromophores (2,4‐diamino‐4′‐(4‐ nitrophenyl‐diazenyl)azobenzene (DNDA)) was reacted with excessive amount of 4, 4′‐methylene‐ diphenylisocyanate (MDI) to form poly‐CDI, and subsequently trimellitic anhydride (TMA) was added to obtain poly(N‐acylurea). The organic/inorganic composites containing prepolymer of phenyltriethoxysilane (PTEOS) and poly(N‐acylurea) in different weight ratios (10:90, 30:70, 50:50, 70:30, 90:10 wt%) were prepared, respectively. The moderate glass transition temperature (Tg) characteristic of the poly(N‐acylurea) allows the NLO‐active polymer to achieve high poling efficiency. After in situ poling and curing process, the Tgs of the composites were elevated, and higher than that of the pristine poly(amide–imide) sample. Electro‐optical (EO) coefficients (r33) of about 5.5 ∼ 18.0 pm/V at 830 nm were obtained. Excellent temporal stability at 100°C, and waveguide characteristics (3.1–4.2 dB/cm at 830 nm) were also obtained for these composites. Copyright © 2008 John Wiley & Sons, Ltd.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call