Abstract
ABSTRACTIn this work we have investigated the magnetic and structural properties of spin-valve films exchange biased by CoFe/NiMn compared to CoFe/lrMn spin valves. A spin-valve film of structure Ta/NiFe/CoFe/Cu/CoFe/NiMnITa showed a giant-magnetoresistance of 5.5% with a Hex∼850 Oe after annealing. Structural ordering of the NiMn in an fct phase after annealing has been observed using x-ray diffraction, with the data exhibiting pure fct(111) texture. The thermal stability of both the exchange pinning and magnetoresistance of NiMn spin-valves was evaluated. The blocking temperature (Tb) of this film is 400°C, compared to 225°C for IrMn based spin-valve films (IrMn thickness ∼50 Å). Blocking temperature distribution and remnant blocking temperature measurements also suggest that NiMn based spin-valves have far superior pinning stability with temperature than IrMn based spin-valves. Magnetoresistance measurements show a linear decrease with temperature due to electron-phonon scattering with the ∆R/R being reduced by 33% at 150°C (as compared to a 50% decrease for IrMn based spinvalves). Extended annealing at 150°C did not effect spin-valve performance, with ∆R/R and R being constant over 60 hours, suggesting that no appreciable interdiffusion is occurring.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.