Abstract
A telechelic organic–inorganic polymer (SiPPSU) where –SiPh(OH) 2 groups are covalently linked to the polymeric chain of polyphenylsulfone (PPSU) was prepared and characterized. The polymer was sulfonated up to a degree of sulfonation (DS) equal to 2 (SiSPPSU), then used to prepare blends with sulfonated polyetheretherketone (SPEEK) having DS = 0.9 in 5 and 10 wt.% concentration. The synthesized polymers and the blends were characterized by ATR/FT-IR spectroscopy. Membranes were prepared with these materials and their proton conductivity was measured using electrochemical impedance spectroscopy (EIS). The formation of the blends substantially altered the physicochemical characteristics of SPEEK: the membrane prepared with the blend at the concentration of 5 wt.% exhibited high and stable conductivity values at 120 °C: both when dry ( σ = 6.1 × 10 −3 S/cm) and wet conditions ( σ = 6.4 × 10 −2 S/cm for a 50% water uptake), hence, being suitable for application as electrolyte in intermediate temperature polymer electrolyte membrane fuel cells (PEMFCs).
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call