Abstract
Nano titanium dioxide TiO2 was synthesized using hydrolysis method then subjected to several characterizations. XRD revealed that the as-prepared sample is pure anatase phase and after calcinations at 500°C for 3h the crystallinity has increased. The crystallite size calculated by Debye–Scherrer’s formula is 8nm. The HRTEM image shows an average size of about 9nm, which is close to the XRD calculation from Scherrer’s formula. PM3 semiempirical quantum mechanical calculations were conducted to present the electronic as well as thermal properties for TiO2. FTIR spectra between 800 and 400cm−1 are the verification for the lattice vibrations of anatase TiO2. The photo catalytic degradation of methylene blue (MB) was tested by the prepared nano TiO2. Results indicate that, the maximum degradation efficiency reached 94.4% after 120min of UV irradiation. This increase in the degradation efficiency of TiO2 could be attributed to the reduction in particle size that enhanced the crystallinity as a result of heat treatment.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call