Abstract
The structure and mechanical properties of materials fabricated by spark plasma sintering of mechanically activated mixture of nickel and aluminum nanopowders were investigated. On account of the elemental powders ratio formation of Ni3Al compound was expected. Relative density of sintered samples was equal to ~ 95 %, microhardness of materials was 6540 MPa. Ultimate tensile strength of samples tested according to three-point bending scheme exceed 1100 MPa.