Herein, bulk La1-xSrxB6 hexaborides with >96.5% in relative densities have been fabricated by SPS, and the phase composition, microstructure, mechanical and thermionic emission properties are investigated. The sintered specimens with average grain sizes of about 14 μm are determined to be CsCl-type single-phase solid solutions without any detectable impurities or other secondary phases. The homogenous elemental distributions of La and Sr have been confirmed at both microscale and nanoscale. The Vickers hardness (18–23 GPa) of these sintered specimens are higher than LaB6, while the indentation fracture toughness (about 2.00 MPa m1/2) are comparable to LaB6. The nanoindentation hardness and Young's moduli have been measured to be 26–30 GPa and 380–400 GPa, respectively, by nanoindentation tests at a maximum load of 20 mN. Only from the perspective of work function, bulk La1-xSrxB6 hexaborides with lower work functions and higher thermionic emission current densities than LaB6 have a potential to be a class of excellent hot cathodes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.