Abstract
A series of samples of hexagonal boron nitride-aluminum nitride (10-90, 15-85, 20-80, 25-75, 30-70wt.%) ceramic composites were prepared by spark plasma sintering in a nitrogen atmosphere at 1650 °C-1800 °C for 5min. Different amounts of CaF2 were added as sintering aids. The effects of CaF2 and sintering temperature on densification and dielectric properties were discussed. The addition of CaF2 enhances relative dielectric constant and loss tangent of the samples. The increase in sintering temperature promotes the densification and decreases the dielectric loss tangent. When being sintered at 1700 °C, the relative density, dielectric constant and dielectric loss tangent of the sample with 15wt.%BN are 98.04%, 7.15 and 6.31×10-4 respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.