Abstract
The low-temperature (less than or equal to 550/sup 0/C), low-pressure (less than or equal to 36 torr) hydrogen absorption characteristics of specific types of Zircaloy-4 internal cladding surfaces (pickled, machined and welded) were investigated. The highest hydrogen contents were found at the machined and abraded surfaces. Although the pickled surface film on Zircaloy-4 retarded hydrogen pickup, especially at lower temperatures (less than or equal to 400/sup 0/C) and very low hydrogen pressures (less than or equal to 3.5 torr), some hydrogen was absorbed through the film even under these conditions. More hydrogen penetrated the pickled surfaces at higher temperatures and pressures. The pickled surfaces absorbed the hydrogen uniformly and without localization even with some film imperfections present. Little hydriding occurred when etched and welded Zircaloy-4 surfaces were exposed to water vapor at corrosion temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.