Solution Growth of <i>p</i>-Type 4H-SiC Bulk Crystals with Low Resistivity

Abstract

P-type 4H-SiC bulk crystals have been grown at a high growth rate of 1.0 mm/h by solution growth using Si-Cr-Al based melt. The crystals grown from solution with an Al content of 10at% show low resistivity of 35 mcm, which is two orders of magnitude lower than commercialwafers (Resistivity: 2500 mcm). The low-resistivity crystals have flat surface and few solvent inclusions. These results indicate that solution growth is a suitable method for fabricating low-resistivity p-type substrates with low cost.