Solid-Phase Epitaxial Regrowth and Dopant Activation of Arsenic. Implanted Metastable Pseudomorphic Ge0.08Si0.92 AND GeO.16SiO.84 ON Si(100)

Abstract

ABSTRACTMetastable pseudomorphic GexSi1−x (x=8%,16%) films were deposited on p-Si(100) substrates by chemical-vapor-deposition and then implanted at room temperature with 90 keV arsenic ions to a dose of 1.5×1015/cm2. The implantation amorphizes approximately the top 125 nm of the 145 nm-thick GeSi layers. The Si-GeSi interfaces remain sharp after implantation. Implanted and non-implanted GeSi samples, together with implanted Si control samples, were subsequently annealed simultaneously by rapid thermal annealing in a nitrogen ambient at 600,700,800 × for 10,20,40s at each temperature. The implanted samples undergo layer-by-layer solid-phase epitaxial regrowth during annealing at or above 600 ×C. The amorphized and regrown GeSi layers are always fully relaxed with a very high density of dislocations (1010-1011/cm2). At a fixed annealing temperature, strain relaxation of an implanted GeSi film is substantially more extensive than that of a non-implanted one. About 50-90% of the implanted arsenic ions become electrically active after the completion of solid-phase epitaxy. The percentages of arsenic ions that are activated in the Si control samples are generally higher than those in GeSi. The room-temperature sheet electron mobility in GeSi is roughly 30% lower than that in Si for a given sheet electron concentration. We conclude that metastable GeSi on Si(100) amorphized by arsenic ions and recrystallized by solid-phase epitaxy cannot recover both its crystallinity and its pseudomorphic strain under rapid thermal annealing.