Abstract
Differential Thermal Analysis (DTA) and Directional Solidification and Quenching (DSQ) were used to evaluate the solidification and precipitation sequence for the Ni-base superalloys IN718, IN625 and IN939. They all showed a similar precipitation sequence, with an initial precipitation of gamma dendrites, followed by an intermediate non-invariant divorced eutectic reaction of type L -> gamma + MC, and a final eutectic precipitation of Laves phase for alloy IN718 and IN625 and of eta-phase for alloy IN939. The reaction temperatures and the amounts of carbides and of final precipitates were evaluated. Precipitated nitrides were found to act as nucleation sites for the precipitation of blocky carbides/carbonitrides, at low interdendritic supersaturation, while in interdendritic regions with high supersaturation, a 'script-like' carbide formation was found instead.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.