Abstract
A 4Kg grade AlCoCrFeNi2.2 high entropy alloy was prepared by low vacuum medium frequency induction melting. The microstructure results showed that the microstructure and composition of the ingot were uniform. The microstructures were composed of primary Ni-rich FCC phase and eutectic structure. The eutectic structure was composed of Ni-rich FCC phase and Al-rich B2 phase. The hardness results showed no significant difference in Vickers hardness between different parts of the ingot, and fluctuated within the range of HV260 ± 20. The compression test results showed that there was no significant difference in compression performance between different parts of the ingot. The AlCoCrFeNi2.2 high entropy alloy had excellent compression performance, the yield strength reached 600 MPa, the fracture strength reached 2200 MPa, and the compression ratio was greater than 40%. Above all, the near-eutectic AlCoCrFeNi2.2 high-entropy alloy had the characteristics of good casting ability, high strength, good plasticity, and was easy to realize the preparation of large-volume non-segregation ingot.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call