Solid-state poly(methyl methacrylate) (PMMA) nanofoams. Part II: Low-temperature solid-state process space using CO2 and the resulting morphologies

Abstract

In this paper, solid-state poly(methyl methacrylate) (PMMA) nanofoams are fabricated via a low-temperature CO2 saturation process. Nanofoams with smallest cell size in 30–40 nm range and cell nucleation densities exceeding 1014 cells/cm3 are achieved. We investigated the effect of saturation temperature on the solid-state foaming of PMMA and resulting morphologies of the foams in the range of −30 °C to 40 °C. A range of equilibrium mass% of CO2 are achieved via the different saturation temperatures, from 11.4% at 40 °C to 39.3% at −30 °C. The amount of CO2 absorbed greatly influences cellular structure of PMMA foams. We identify a critical mass% CO2 window between 30.1% and 32.6%, within which cell nucleation density rapidly increases and consequently foamed microstructure changes from microcellular to nanocellular. Nanofoams with void fraction as high as 86% are created. A transition from closed nanocellular structure to bicontinuous nanoporous structure, and also novel worm-like nanostructures have been observed.