Solid state NMR characterization of formation of poly(ε-caprolactone)/maghnite nanocomposites byin situ polymerization

Abstract

Results of multinuclear MAS NMR spectroscopy are reported for poly (ε-caprolactone)/maghnite nanocomposite formation, with ε-caprolactone in situ polymerized in the presence of maghnite, a proton exchanged montmorillonite clay. Exfoliated and intercalated materials with different maghnite loading in the range 3–15 wt % were investigated. 1H NMR evidences Brønsted acid hydroxyl groups in the silicate layers and shows that their broad signal at 7.6 ppm present in the parent clay disappears in the nanocomposite material. 27Al MAS NMR results show that beside the hexacoordinated aluminum signal, two additional peaks corresponding to two different tetrahedral Al sites are present in the clay framework. The NMR signal intensity of only one of them was found to be affected in the nanocomposites compared with the parent maghnite, suggesting that these specific aluminum sites are the reactive ones at the initial stages of the polymerization. However almost no changes occurred in the 29Si NMR spectra, confirming that the polymer grafting, as indicated earlier by atomic force microscopy, took place on the aluminum tetracoordinated sites rather than on the silicon sites. A mechanism of maghnite surface catalyzed polymerization of ε-caprolactone was proposed, involving Brønsted and Lewis acid sites. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 3060–3068, 2007