Abstract

Considering that ZnAl2O4 spinel has two different sites (octahedral and tetrahedral) and its properties change with dopant ion distribution among these two sites; ZnAl2O4 doped with varied concentrations of Fe(3+) was synthesized by a low temperature sol-gel combustion method. Phase purity and structural investigations were carried out using Rietveld refined X-ray diffraction which shows a decrease in the value of cell parameters at higher doping levels. Photoluminescence (PL) and electron paramagnetic resonance (EPR) studies have shown that on doping, Fe(3+) ions were distributed in both tetrahedral and octahedral sites. At octahedral sites, Fe(3+) exhibited a broad red emission around 745 nm while at tetrahedral sites it exhibited well-defined vibronic sidebands at 665, 674, 684 and 693 nm along with a broad blue band with a maxima at 445 nm at room temperature. EPR studies have shown a broad spectrum at g ≈ 2.2 which corresponds to the Fe(3+) in octahedral sites, while the broad signal at g ≈ 4.2 belongs to Fe(3+) in tetrahedral sites. It was also inferred from these studies that Fe(3+) prefers to occupy octahedral sites at higher concentrations and at higher annealing temperatures. The PL decay behavior of Fe(3+) in ZnAl2O4 has also shown that two different types of Fe(3+) ions were present in this matrix. The first type was a long lived species (τ ≈ 170 μs) present at octahedral sites and the other was a short lived species (τ ≈ 40 μs) present at the tetrahedral sites; the fraction of the long lived species predominate at higher concentrations. Thus the present work is mainly focused on understanding the tuning of local site occupancy of the dopant ion among those sites with varying concentration and annealing temperature, using the dopant ion itself as a spectroscopic probe, which further helps in understanding the phase (inverse and normal) of the spinel.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.