AbstractSi1-x-yGexCy/Si heterostuctures were formed on Si (100) surface by Ge and C implantation with a high dose rate MEtal - Vapor Vacuum arc (MEVVA) ion source and subsequent Solid Phase Epitaxy (SPE). after thermal annealing in the temperature range from 600 °C to 1200 °C, the implanted layer was studied using Rutherford Back-scattering Spectrometry (RBS), cross-sectional High Resolution Transmission Electron Microscopy (HRTEM) and fourbounce X-ray Diffraction (XRD) measurement. Due to the small lattice constant and wide bandgap of SiC, the incorporation of C into Si-Ge can provide a complementary material to Si-Ge for bandgap engineering of Si-based heterojunction structure. Polycrystals are formed at temperature at and below 1000 °C thermal growth, while single crystal epitaxial layer is formed at 1100 °C and beyond. XRD measurements near Si (004) peak confirm the compensation of the Si1-x Gex lattice mismatch strain by substitutional C. C implantation is also found to suppress the End of Range (EOR) defect growth.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call