Abstract
In the present study, the solid particle erosion behaviour of neat PEEK matrix and unidirectional glass fibre (GF) and carbon fibre (CF) reinforced polyetheretherketone (PEEK) and polyetherketoneketone (PEKK) composites has been studied. The erosion experiments have been carried out by using silica sand particles (200±50μm) as an erodent. Steady state erosion rates of these composites have been evaluated at different impact angles and impact velocities. The neat PEEK exhibited peak erosion rate at 30° impingement angle whereas the composites exhibited a semi-ductile behaviour with peak erosion rate at 60° impact angle. The erosion rate of the glass fibre reinforced composites was higher than that of the carbon fibre reinforced composites. The results show that the fibre orientation has a significant influence on erosion rate only at lower impact angles. The erosion rate of the composites was higher when the particles impact perpendicular to the fibre direction than parallel to the fibres. The morphology of eroded surfaces was observed under scanning electron microscope and damage mechanisms were discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.