Abstract
Bi2WO6 and Bi2WO6/graphene thin films were fabricated by spin coating and post annealing at 600 °C for 2 h. In four different thin film samples, the graphene concentration was controlled as 0, 2, 4 and 6 wt%, respectively. The morphology, grain size and elemental distribution of the thin films were characterized by SEM and TEM. The crystallization and crystal phases were determined by XRD patterns, and the existence of graphene in Bi2WO6/graphene composite thin films were confirmed by Raman spectra. The photocatalytic performance of Bi2WO6 and Bi2WO6/graphene thin films was investigated by oxidizing NO under visible light irradiation. The results showed that Bi2WO6/graphene with 4 wt% of graphene showed the highest photocatalytic performance among all samples. This could be attributed to the increased electron conductivity with the presence of graphene. However, a further increased graphene concentration resulted in a decreased photocatalytic performance.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.