Abstract
As the oxygen redox ability shows great effects on the catalytic performances of ceria-zirconia based materials, many strategies have been utilized to improve the oxygen storage capacity. Here in this study, we report a simple and facile approach to prepare a SO42–-modified La, Y-doped ceria-zirconia material (SO/CZLY-f) with high oxygen storage capacity. Due to the additional redox process between SO42− and S2−, oxygen storage capacity of SO/CZLY-f (745.3 μmol O2/g) is about 1.6 times higher than that of La, Y-doped ceria-zirconia material without SO42– modification. Moreover, the catalytic activities and stability of the corresponding Pd-only three-way catalyst were measured. Compared to that of Pd@CZLY-f, the operation window of CO, full conversion temperature of HC and NO over Pd@SO/CZLY-f are obviously widened and lowered, respectively. After aging treatment at 1100 °C for 4 h, the superiority of aged Pd-loading composite is still maintained.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call