Abstract
Trace level methane (CH4) detection is demonstrated at low temperature. Functional metal oxide of SnO2 tailored by CuO is prepared via a co‐precipitation chemical route followed by annealing in air. Raman spectroscopy confirms presence of Ag mode of CuO at 290 cm−1 along with A1g mode of SnO2 at 630 cm−1. Results from the X‐ray diffraction and transmission electron microscope indicate that both crystalline SnO2 and CuO are present in the composite. Particle size of SnO2 is found to be larger in the composite than the pristine‐annealed SnO2 of 25 nm at 800 °C. However, sensor studies with CH4 reveal stronger response and low operational temperature of 100 °C for the composite in comparison to the pristine‐annealed SnO2 which shows poor response (<1%) even at higher temperature of 150 °C. Current–voltage measurements support the formation of local p–n junctions in the CuO–SnO2 composite. The role of n–p junction in the composite is elaborated and correlated to the improved response.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have