Abstract
Herein, CdTe/MnS core/shell nanoparticles dispersed in an aqueous solution have been synthesized. The formation of MnS semiconductor shell occurs by spontaneous self‐assembly. This process is activated by thermal hydrolysis that removes the excess of thiol and releases S2− ions. In this process, Mn2+ ions on the surface of the CdTe nanoparticles bind to S2− ions to produce a fine semiconducting layer of MnS. Measurements of Raman spectroscopy, optical absorption, and electrochemical measurements are performed. The Raman spectrum shows CdTe characteristic bands at 141 and 163 cm−1. Bands at 221 and 444 cm−1 are associated with the MnS structure. Cyclic voltammetry and differential pulse voltammetry are used to estimate the electrochemical gap at ≈2.47 eV. Absorption optical measurements show tree absorption bands. A broad band between 460 and 520 nm is associated with the first transition in CdTe nanoparticle. The absorption spectrum reveals an optical gap in the range of 2.41–2.33 eV for all the refluxed samples. These values are consistent with those obtained with the electrochemical measurements. The results evidence the formation of a core–shell semiconducting nanostructure made of CdTe nanoparticles coated with a spontaneously self‐assembled thin layer of MnS nanoparticles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.