Abstract
Cubic Co3O4 nanoparticles with average diameters of 5.9, 21.1, and 46.9 nm (hereafter small, medium, and large) have been synthesized and characterized by pXRD, TEM, and BET. The nanoparticles were loaded onto Ni foam supports for evaluation as anodes for water electrolysis in 1.0 M KOH. Current densities of 10 mA/cm2 were achieved at overpotentials of 328, 363, and 382 mV for anodes loaded with 1 mg/cm2 of small, medium, and large sized Co3O4 nanoparticles, respectively. The activity correlates with the BET surface area of the isolated particles. A plot of the electrochemical overpotential at 10 mA/cm2 against the log of the BET surface area gives a linear relation with a slope of −47 ± 7 mV/dec, showing unequivocally that the activity increase is a function of accessible catalyst surface area.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.