Abstract
The method of controlling the size of a poly(2-oxy-6-naphthoyl) (PON) whisker was examined with a focus on lengthening the whisker. PON whiskers were prepared by the polymerization of 2-acetoxy-6-naphthoic acid in liquid paraffin at 330°C. The whiskers were very symmetrical. and both tips were very sharp. Growth of the whiskers along the length took place by which oligomer lamellae piled up along the long axis of the needlelike crystals with spiral growth. During steady growth until 8 min, the tip angle of the whiskers was constant at 80°. However, it became significantly sharper (22°) at 30 min, and later the trunk part of the whiskers stopped increasing. To depress the sharpening of the tips and to extend the steady-growth period for longer whiskers, oligomers were added to the polymerization system after 8 min, just before the tip angle became sharper, to keep the concentration of the oligomers in the polymerization system constant. The addition of the oligomers extended the steady-growth period, and the length increased from 12.5 to 17.3 μm. Although the width of the whiskers increased very slightly with the addition of the oligomers, the axial ratio of the whiskers increased from 19.4 to 24.7. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1320–1327, 2003
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.