ABSTRACTThe influence of the microstructure of uniaxial cold-compacted green iron on the sintering shrinkage was investigated. Pores in the green parts are very slightly oriented, while the dimension of the interparticle contact areas is anisotropic. A large and anisotropic anisothermal shrinkage in alpha iron was measured, greater than isothermal shrinkage at the 1120°C. The results were interpreted on the basis of the geometrical and of the structural activity, and the effective diffusivity responsible for neck growth was determined.