Abstract
Several boride sintered bodies such as TiB2, ZrB2, and SiB6 were previously reported. In the present study, the sinterability and physical properties of chromium boride (CrB2) containing chromium carbide (Cr3C2) sintered bodies were investigated in order to determine its new advanced material. The samples were sintered at desired temperature for 1 hour in vacuum under a pressure by hot pressing. The relative density of sintered bodies was measured by Archimedes’ method. The relative densities of CrB2 addition of 0, 5, 10, 15 and 20 mass % Cr3C2 composites were 92 to 95 %. The Vickers hardness of the CrB2 with 10 and 15 mass % Cr3C2 composites were about 14 and 15 GPa at room temperature, respectively. The Vickers hardness at high temperature of the CrB2 addition of 10 mass % Cr3C2 composite decreased with increasing measurement temperature. The Vickers hardness at 1273 K of the sample was 6 GPa. The Vickers hardness of CrB2 addition of Cr3C2 composites was higher than monolithic CrB2 sintered body. The powder X-ray diffraction analysis detected CrB and B4C phases in CrB2 containing Cr3C2 composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.