Abstract
Co67Ni33 microspheres and Ni0.6Zn0.4Fe2O4 nanocrystals were synthesized by hydrothermal method. The complex permeability and complex permittivity of the as-prepared powders dispersing in wax (60wt% powder) were measured using a vector network analyzer in 2–18GHz frequency range. The calculated microwave absorption of single-layer and double-layer absorbers based on Co67Ni33 microspheres and Ni0.6Zn0.4Fe2O4 nanocrystals were analyzed in 2–18GHz frequency range. The results show that the Ni0.6Zn0.4Fe2O4nanocrystals with the relatively low permittivity and Co67Ni33 microspheres with the relatively high dielectric loss and magnetic loss can be used as proper matching layer and excellent absorption layer, respectively. The double-layer absorber with a coating thickness of 2.1mm exhibits a maximum reflection loss of −43.8dB as well as a bandwidth (reflection loss less than −10dB) of 5GHz. Moreover, their absorption peak and the absorption intensity can be adjusted easily through changing the stacking order and each layer thickness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.