Abstract
AbstractAmino‐modified silica nanoparticles (SiO2─NH2) were first prepared by hydrolytic condensation of tetraethyl orthosilicate and 3‐aminopropylmethyldiethoxysilane. Then, organic–inorganic hybrid particles (SiO2─SMA) were prepared by the amidation reaction between SiO2─NH2 and poly(styrene‐alt‐maleic anhydride) (SMA). Subsequently, SiO2─SMA particles were employed for modifying bisphenol‐A epoxy/anhydride thermoset. Compared with pure cured epoxy, the modified epoxy thermosets with only 1 wt % of SiO2─SMA particles could achieve a simultaneous toughening and reinforcing performance. The tensile strength, impact strength, and fracture toughness of epoxy thermoset were increased by 14.1, 44.3, and 114.4%, respectively. Moreover, the modification also improved the thermal stability of epoxy thermosets, and the modulus and glass transition temperature of cured resin were not sacrificed. It can be attributed to the rigid structure of SiO2, as well as the anhydride and carboxyl groups onto the surface of SiO2─SMA particles participating in the epoxy curing reaction and effectively enhancing the crosslinking density of epoxy thermoset.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.