Abstract
Shear punch mechanical testing was performed on neutron-irradiated HT-9 and 14YWT alloys, comparing the traditional ferritic/martensitic steel with the advanced oxide dispersion strengthened nanostructured ferritic alloy. The samples were irradiated at various temperatures between 380°C and 520°C. In HT-9, on increasing the irradiation temperature, the 1% offset shear stress and maximum shear stress decreased. The advanced 14YWT alloy was less sensitive to irradiation temperature with respect to irradiation hardening. However, it still exhibited irradiation hardening at each temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.