Abstract
The irradiation hardening response of five metals irradiated in RTNS-II was investigated using a combination of ball microhardness and shear punch test techniques. The specimens were transmission electron microscopy disks of pure nickel, Ni-5wt%Si, pure iron, solution annealed prime candidate alloy (PCA) for Path A, and 40% cold worked MFE 316 stainless steel. Specimens were irradiated in RTNS-II to fluences in the range 6 × 10 16 to 6 × 10 17 n/cm 2 . Only limited ball microhardness data could be obtained because of disk thickness. However, the ball microhardness data obtained were in good agreement with shear punch data. It was found that the pure metals exhibited little hardening after exposure to fluences of ~1 × 10 17 n/cm 2 , but Ni-5 Si exhibited significant hardening after 6 × 10 17 n/cm 2 . Hardening in PCA was similar to that observed in solution annealed 316 stainless steel; and hardening in 40% cold worked MFE 316 was relatively small after 6 × 10 17 n/cm 2 . The Ni-5 Si response may be due to irradiation induced precipitation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.