Shape-Selection of Thermodynamically Stabilized Colloidal Pd and Pt Nanoparticles Controlled via Support Effects

Abstract

Colloidal chemistry, in combination with nanoparticle (NP)/support epitaxial interactions is used here to synthesize shape-selected and thermodynamically stable metallic NPs over a broad range of NP sizes. The morphology of three-dimensional palladium and platinum NPs supported on TiO2(110) was investigated using scanning tunneling microscopy. Well-defined Pd and Pt NPs were synthesized via inverse micelle encapsulation. The initially spherical NPs were found to become faceted and form an epitaxial relationship with the support after high-temperature annealing (e.g., 1100 °C). Shape selection was achieved for almost all Pd NPs, namely, a truncated octahedron shape with (111) top and interfacial facets. The Pt NPs were however found to adopt a variety of shapes. The epitaxial relationship of the NPs with the support was evidenced by the alignment of the cluster’s edges with TiO2(110)-[001] atomic rows and was found to be responsible for the shape control. The ability of synthesizing thermally stable shape-...