Abstract
In current work, the deformation behavior and deformed microstructures of GH3536 superalloy in semi-solid state were investigated, and the semi-solid flow stress was predicted by artificial neural network (ANN) model. The semi-solid compression deformation was carried out at 1320-1350 °C, and the solid deformation behavior at 1200 °C was tested for comparison. The peak stress under 0.01-1 s-1 semi-solid deformation was 45.6-161.9 MPa. The peak stress decreased with the increase of deformation temperature and the decrease of strain rate. The ANN model could well describe semi-solid flow stress. During semi-solid deformation, the apparent viscosity dropped as shear rate increased. At high temperature and low strain rate, more liquid phase was distributed at grain boundaries. The solid grains coarsened as deformation temperature increased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.