Abstract
(C5H5)2Fe and Fe(CO)5 were used as the 3d transition-metal dopant sources in the growth of semi-insulating InP epitaxial layers by low-pressure metal-organic chemical vapour deposition (MOCVD). From the bright- and dark-field images of transmission electron microscopy (TEM) analysis, many precipitates were observed. Three extra peaks in the X-ray diffraction pattern were found. The peaks of band-band recombination, donor-acceptor pair recombination transitions and the recombination of donor-acceptor pair with one-phonon emission were observed in the short-wavelength range of low-temperature photoluminescence measurement. Three Fe-related peaks were observed at 0.7079, 0.6897 and 0.6683 Ev. For a wide range (10–600) of In/Fe molar fraction, the resistivity remained at high values (about 108 Ω cm) and the highest resistivity appeared at 5 × 108 Ω cm for a 1 Μm layer with a breakdown voltage of 9 V.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.