Abstract
Abstract Cupronickel pipes are widely used in cooling systems. Under this application, localized corrosion is observed, particularly associated with selective corrosion of nickel (denickelification). This work studied the denickelification process in solution-treated cupronickel alloys 90-10 (Cu-10wt%Ni), with aluminum and iron additions, in 0.01 M, 0.1 M, or 0.6 M sodium chloride (NaCl) aqueous solutions. Polished surfaces of the studied materials were submitted to potentiodynamic polarization, and after that, the polarized surfaces were studied using optical microscopy (OM) and scanning electron microscopy (SEM) assisted by energy-dispersive spectroscopy (EDS). A passivity break potential (Epb) was determined in all solutions, related to the initiation of selective corrosion of nickel. When submitted to cyclic potentiodynamic polarization, alloys with higher Epb showed the higher nickel losses in localized spots. However, potentiodynamic polarization tests conducted in 0.01 M NaCl until current densitie...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.