Abstract
The segregation of minor components such as flow agents, in an industrial coil coating based on epoxy resins crosslinked with a urea formaldehyde resin and applied to a hot-dipped galvanized steel (HDGS) substrate, has been investigated by high resolution XPS. The addition of a low amount of flow agent in the coating formulation leads to changes in the surface elemental composition. High-resolution monochromated XPS C1s spectra can be peak-fitted taking into account all functionalities of the respective components of the formulation. The examination of both the elemental and chemical surface compositions clearly demonstrates that the use of flow agent in the process leads to its preferential segregation towards the air–film interface. This result is interpreted in terms of minimisation of the surface free energy of the final coil coating. It is also possible to monitor the extent of crosslinking undergone within the coil coating system, using the peak-fitting in the same manner as above, and it was concluded that the system is fully crosslinked.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Electron Spectroscopy and Related Phenomena
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.